20CrMnTi Seamless Pipe

Strict quality control system and perfect after-sales service system are always our top concern which can guarantee and track the quality of our products from raw materials procurement, production processes, finish products as well as after-sales service.

Customization

Test:SGS or Third- party test

Delivery: 5-7days after deposit

More Details

20CrMnTi is carburized carbon steel, carburized carbon steel is usually 0.17%-0.24% carbon content of low carbon steel. It is Cr Mn Ti steel in medium hardenability carburized carbon steel. Its hardenability is high. Under the condition of ensuring quenching, it especially has high low temperature impact toughness. 20CrMnTi surface carburizing hardened steel. Good machinability, small deformation and good fatigue resistance.

Technical Parameter

 Chemical Composition

Grade

C

Mn

Si

Cr

Ti

20CrMnTi

0.17-0.23

0.80-1.10

0.17-0.37

1.00-1.30

0.04-0.10

Quality

S

P

Cu

Ni

 

High-quality
steel

≤0.030

≤0.030

≤0.030

≤0.030

 

High-grade fine steel

≤0.020

≤0.020

≤0.025

≤0.030

 

Super grade steel

≤0.010

≤0.020

≤0.025

≤0.030

 

Mechanical Property

Grade

Tensile
Strength
σb(MPa)

Yield
Strength
σs (MPa)

Elongation
δ5 (%)

Reduction  
of area
ψ(%)

Hardness

Akv
 (J)

αkv (J/cm2)

20CrMnTi

≥1080(110)

≥835(85)

≥10

≥45

≤217HB

≥55

≥69(7)

Sample size: sample blank size is 15mm

Conventional Parameters

OD

20-500mm

Length

5.8-12m

Thickness

0.5-40 mm

Alloy or not

Alloy

Tolerance

±0.5%

Payment term

T/T (30% Deposit)

MOQ

5Tons

Packing

Standard Sea-worthy Packing

Standard

AISI,ASTM,DIN,JIS,GB ,JIS,SUS,EN,etc

Usage

It is a good performance of carburizing carbon steel, high hardenability, after carburizing quenching with hard and wear-resistant surface and tough core, with high low temperature impact toughness, weldability, good machinability after normalizing. It is used to manufacture the important parts such as gear, gear ring, gear shaft cross head which bear high speed, medium or heavy load, impact and friction with cross section <30mm. Is a substitute steel for 18CrMnTi, widely used as carburized parts in automobiles. The tractor industry is used in cross sections below 30mm to withstand high speeds. Medium or heavy load and impact. Friction of important carburized parts, such as gears. Shaft. Gear ring. Gear shaft. The main shaft of the sliding bearing. Crosshead. Claw clutch. Worm, etc.

Chemical composition editing